一種新型疏水締合聚合物的研究



摘   要

　　　由于疏水締合聚合物的疏水締合作用，其水溶液表現(xiàn)出良好的增粘效應、剪切變厚、在鹽存在和高溫的條件下能保持較高的粘度。

　　　本文采用水溶液聚合的方法，以AM、AMPS、和十八烷基二甲基氯化氨為主要原料合成一種新型的疏水締合聚合物。并在實驗室條件下測定和探討了它的溶液性質，證明了它是一種具有較好的流變性、抗溫抗鹽性及高效增粘性的疏水締合聚合物。最后簡要分析了其在鉆井液、涂料中的運用。

　　　

　　　

　　　

關鍵詞：疏水締合聚合物   十八烷基二甲基氯化氨   AMPS   溶液性質

Abstract

　　　

　　　

　　　Because of the function of the Hydrophobically associating water-soluble polymers, their solutions have good properties due to the hydrophobic groups. Such as: high effective viscosifying, shear thinning, thermo and slat resistance and so on.

　　　This passage have synthesized the new Hydrophobically associating water-soluble polymers with the method of aqueous solution by composing of AM AMPS and a new   hydrophobic monomer. We have measured and analysized the properties of polymer solution under the laboratory conditions. Then we have proved out it have the good function of high effective viscosifying, shear thinning, thermo and slat resistance by analysising. At the same time, we have compendious analysised it’s use in drilling fluid, dope and so on. Finally, we had the conclusion that it is a good Hydrophobically associating water-soluble polymers

　　　

　　　

　　　


 


Key word: Hydrophobically associating water-soluble polymers, an new ahydrophobic monomer, AMPS, properties of polymer solution

　　

　　　　　　

　　　　　　

　　　　　　

　　　　　　　　　　　　　　　　　　　　目錄

摘   要 1

Abstract 2

1前言 5

1.1疏水締合聚合物簡介 5

1. 2疏水締合聚合物發(fā)展簡史與合成方法 5

1.2.1發(fā)展簡史 5

1.2. 2合成方法 7

1.3疏水締合水溶性聚合物分子設計原理 8

1.4聚合物的結構及組成 10

1.4.1疏水基團：十八烷基二甲基丙烯基氯化銨 10

1.4.2 AMPS 11

1.4.3AM 12

1.5合成路線 12

1.6研究目的 14

2 實驗部分 14

2.1藥品與儀器 14

2.1.1藥品 14

2.1.2儀器 15

2.2實驗室制備 15

2.2.1單體制備 15

2.2.2聚合物的制備 16

2.2.3疏水締合性能測定 17

2.2.4抗溫性能測定 18

2.2.5抗鹽性能測定 18

2.3產物鑒定 19

2.3.1十八叔胺鑒定 19

2.3.2疏水單體的鑒定 19

2.3.3疏水締合聚合物的鑒定 19

3實驗結果與討論 21

3.1疏水締合聚合物粘濃變化 21

3.2疏水基團含量與表觀粘度 23

3.3疏水締合性能評價 24

3.4聚合物的抗鹽性能評價 26

3.5聚合物的抗溫性能評價 29

4.疏水締合聚合物的應用分析 32

4.總結 33

致謝 34

參考文獻 35