隨著經濟的快速發(fā)展，我國開始進入城市化和機動化的加速發(fā)展階段。目前在我國形成了以地鐵、城市快速鐵路、高架輕軌等為主的多元化發(fā)展趨勢。錨固螺栓是輕軌軌道線路設備的重要部件，如果錨固螺栓失效，將會嚴重影響輕軌的運行安全。因此，研究軌道錨固螺栓失效的原因具有重要的現(xiàn)實意義。
本論文著重從以下幾個方面進行研究：
1．從受力及疲勞角度出發(fā)分析錨固螺栓斷裂的原因。
2．用有限元法分析錨固螺栓的應力分布，查找斷裂原因。
3．分析錨固螺栓所用材料，查找斷裂原因。
4．分析錨固螺栓熱處理工藝，查找斷裂原因
5．提出解決方案,使輕軌交通向著更安全更可靠的方向發(fā)展,為某市輕軌的發(fā)展奠定良好的基礎。
通過以上分析，分別從材料的選擇方面、熱處理方面等方面提出提高軌道錨固螺栓疲勞強度的措施。


關鍵詞: 螺栓，材料，熱處理，有限元，疲勞破壞





ABSTRACT

With the rapid economic development in China, our country has begun to enter into a stage of accelerated urbanization and mechanization. Currently in China formed a diversified development trend which represented by subway, urban express rail and elevated light rail. Anchor bolts is an important component of the Anchor bolts light rail line equipment , the failure of anchor bolts will seriously affect the safe operation of light rail. Therefore, research about the causes of the failure of anchor track bolts is of great practical significance.
This paper makes a research focusing on the following aspects:
1. Analysis of the fracture reasons of track anchor bolts from the Stress and fatigue perspective.
2. Analysis of the stress distribution of track anchor bolts by the way of finite element, find out the fracture reasons.
3. Analysis of the using materials of track anchor bolts as well as the fracture reasons.
4. Analysis of the heat treatment process of track anchor bolts, and finding out the fracture reasons.
5. Propose solutions which enable light rail traffic developed in a more secure, more reliable direction. So to laid a solid foundation for the development of light rail in ChongQing
Through the above analysis to put forward the measures to increase the track anchor bolts fatigue through many perspective, for instance, the choice of materials, heat treatment process, etc.


Key words: Bolt, materials, heat treatment, finite element, fatigue damage






目 錄

中文摘要 Ⅰ
ABSTRACT Ⅱ
1緒論 1
1.1 課題的研究意義 1
1.2 國內外研究概況和發(fā)展趨勢 5
1.3 本課題研究的主要內容 6
2軌道錨固螺栓受力分析 7
2.1 R=500時錨固螺栓受力分析 9
2.2 R=∞時錨固螺栓受力分析 12
2.3 R=100時錨固螺栓受力分析 15
2.4 受力分析結論 18
3軌道錨固螺栓疲勞強度分析 19
3.1 錨固螺栓宏觀疲勞分析 19
3.1.1材料疲勞性能指標 21
3.1.2 錨固螺栓斷口分析…………………………………………………………………21
3.1.3 錨固螺栓疲勞強度計算 23
3.2 軌道錨固螺栓有限元分析 25
3.2.1 錨固螺栓有限元幾何模型的建立 26
3.2.2 有限元網格劃分 27
3.2.3 載荷與邊界條件的建立 28
3.2.4 材料性質的建立 ………29
3.2.5 計算結果及分析 ………29
3.2.6 有限元分析結論 33
3.3錨固螺栓疲勞分析結論及探討 33
4軌道錨固螺栓材料及熱處理工藝分析 35
4.1錨固螺栓的材料分析 35
4.2錨固螺栓的熱處理分析 39
4.2.1淬火溫度對性能的影響 39
4.2.2回火溫度對性能的影響 40
4.2.3不同熱處理后室溫下力學性能分析……………………………………42

4.2.4分析結果 43
5 結論 45
致謝 46
參考文獻 47